专业物性查询
更专业，更放心
更专业，更放心
|
总体
|
|
材料状态
已商用：当前有效
|
|
搜索 UL 黄卡
SABIC
|
|
供货地区
北美洲 ;拉丁美洲 ;欧洲
|
|
用途
Additive Manufacturing (3D Printing)
|
|
加工方法
3D Printing, Fused Filament Fabrication (FFF)
|
|
机械性能
额定值
单位制
测试方法
|
|
拉伸模量
|
|
ZX Orientation
MPa
ASTM D638
|
|
XY Orientation
MPa
ASTM D638
|
|
XZ Orientation
MPa
ASTM D638
|
|
抗张强度 1
|
|
XY Orientation
: 断裂
MPa
ASTM D638
|
|
XZ Orientation
: 断裂
MPa
ASTM D638
|
|
ZX Orientation
: 断裂
MPa
ASTM D638
|
|
伸长率 1
|
|
XY Orientation
: 断裂
%
ASTM D638
|
|
XZ Orientation
: 断裂
%
ASTM D638
|
|
ZX Orientation
: 断裂
%
ASTM D638
|
|
弯曲模量 2
|
|
XY Orientation
MPa
ASTM D790
|
|
ZX Orientation
MPa
ASTM D790
|
|
冲击性能
额定值
单位制
测试方法
|
|
悬壁梁缺口冲击强度
|
|
ZX Orientation
: 23°C
J/m
ASTM D256
|
|
XZ Orientation
: 23°C
J/m
ASTM D256
|
|
XY Orientation
: 23°C
J/m
ASTM D256
|
|
无缺口悬臂梁冲击
|
|
ZX Orientation
: 23°C
J/m
ASTM D256
|
|
XY Orientation
: 23°C
J/m
ASTM D256
|
|
XZ Orientation
: 23°C
J/m
ASTM D256
|
|
可燃性
额定值
单位制
测试方法
|
|
UL 阻燃等级 6
|
|
XZ Orientation
: 1.5 mm
HB
UL 94
|
|
XY Orientation
: 1.5 mm
HB
UL 94
|
|
ZX Orientation
: 1.5 mm
HB
UL 94
|
|
热性能
额定值
单位制
测试方法
|
|
载荷下热变形温度
|
|
XY Orientation
: 1.8 MPa, 未退火, 3.20 mm
℃
ASTM D648
|
|
ZX Orientation
: 1.8 MPa, 未退火, 3.20 mm
℃
ASTM D648
|
|
XZ Orientation
: 1.8 MPa, 未退火, 3.20 mm
℃
ASTM D648
|
|
维卡软化温度
℃
ASTM D1525 4
|
|
维卡软化温度
℃
ASTM D1525 4
|
|
线形热膨胀系数
|
|
流动, XY Orientation
cm/cm/°C
ASTM E831
|
|
横向, XZ Orientation
cm/cm/°C
ASTM E831
|
|
流动, ZX Orientation
cm/cm/°C
ASTM E831
|
|
流动, XZ Orientation
cm/cm/°C
ASTM E831
|
|
横向, ZX Orientation
cm/cm/°C
ASTM E831
|
|
横向, XY Orientation
cm/cm/°C
ASTM E831
|
|
电气性能
额定值
单位制
测试方法
|
|
体积电阻率
|
|
ZX Orientation
ohms·cm
ASTM D257
|
|
XZ Orientation
ohms·cm
ASTM D257
|
|
XY Orientation
ohms·cm
ASTM D257
|
|
介电常数
|
|
XZ Orientation
: 1.90 GHz
2.70
ASTM D150
|
|
ZX Orientation
: 1.90 GHz
2.70
ASTM D150
|
|
XY Orientation
: 1.90 GHz
2.60
ASTM D150
|
|
耗散因数
|
|
XY Orientation
: 1.90 GHz
5.0E-3
ASTM D150
|
|
ZX Orientation
: 1.90 GHz
5.0E-3
ASTM D150
|
|
XZ Orientation
: 1.90 GHz
5.0E-3
ASTM D150
|
|
备注
|
|
1类型 1, 5.0 mm/min
|
|
21.3 mm/min
|
|
3XZ Orientation
|
|
4标准 B (120°C/h)
|
|
5ZX Orientation
|
|
6UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details.
|